Adhesive mixtures must comply with the requirements of the GOST R 56387 standard and be manufactured according to technological documentation approved by the manufacturer. The main indicators of the quality of adhesive mixtures in a dry state are ...
Largest aggregate grain size
Bulk density
Low dust generation
Color
Content of grains of the largest coarseness
Humidity
Material on this issue is presented in the GOST R 56387 .
The symbol of adhesive mixtures must consist of the name of the mixture in accordance with GOST 31189, class designation, values of basic quality indicators (if necessary) and standard designation. Adhesive mixtures are divided into the following classes...
E – mixtures with increased resistance to slipping
C0 – used for laying tiles with normal water absorption (at least 5% by weight) only for interior work
T – quick-hardening adhesive mixtures
S1 – highly elastic mixtures
C1 – used for interior and exterior work and meeting the minimum regulated requirements
F – mixtures with extended open time
C2 - used for interior and exterior work and meeting increased requirements
S2− elastic adhesive mixtures
To mix (dilute, mix) cement adhesive mixtures of class C1, it is necessary to use...
Vegetable oil
Primer
Synthetic oil
Water latex
PVA - emulsion of polyvinyl acetate in water, with a plasticizer and special additives
Water
Adhesive milk
Water-based latex mixture
Material on this issue is presented in technical data sheets for cement adhesive mixtures.
Adhesive mixtures must comply with the requirements of the GOST R 56387 standard and be manufactured according to technological documentation approved by the manufacturer. The main indicators of the quality of adhesive mixtures ready for use (freshly prepared) are ...
Resistance to slippage
Average density
Open time
Water holding capacity
Minimum Density
Maximum Density
What requirements must be met for hardened solutions of adhesive mixtures?
The strength of the adhesive joint after cyclic freezing and thawing must be no less than:
0.5 MPa for C1; 1.0 MPa for C2.
The strength of the adhesive joint after exposure to an air-dry environment for 28 days must be no less than:
0.5 MPa for C0; 0.5 MPa for C1; 1.0 MPa for C2.
The strength of the adhesive joint after exposure to high temperatures must be no less than:
The strength of the adhesive connection to the base of fast-hardening class F adhesives after exposure in an air-dry environment for 6 hours should be no more than 0.5 MPa
The open time to achieve an adhesive joint strength of at least 0.5 MPa should be for adhesives of the following class:
C0 and F – when gluing tiles after 10 minutes; C1 and C2 – when gluing tiles after 20 minutes; E – when gluing tiles after 30 minutes.
The transverse deformation of class S1 adhesives must be at least 2.5 mm, class S2 – at least 5 mm.
The strength of the adhesive joint after exposure to an aqueous environment must be no less than: